THE EFFECT OF PINEAPPLE (ANANAS COMOSUS L. MERR) LEAF FIBER’S VOLUME FRACTION TOWARD FLEXURAL STRENGTH OF FLOWABLE RESIN COMPOSITE

Shilfina Rufaida, Eko Hadianto, Muhamat Muhtar Abdurrohman

Abstract


Background: Composite resin is one of dental restorative materials that have a high aesthetic value. Fiber Reinforced Composite (FRC) is a combination material between polymer matrix and fiber and it is used as an alternative material to improve mechanical properties. The mechanical strength can be affected by the fraction of fiber volume used. This study aims is to know the effect of fraction of pineapple leaf fiber volume to the strength of composite resin flexural with pineapple leaf fiber concentration 0%, 1%, and 1,5%.
Method: This study is a true experimental one with only control group design post-test. The total sample used was 27 specimens with a size 25x2x2 mm. The sample was divided into 3 groups, resin composite with a fraction of pineapple leaf fiber pineapple volume 0%, 1%, 1,5%. Flexural strength was tested by a three-point bending test in the universal testing machine.
Result: The result of flexural strength in flowable resin composite with fraction of pineapple leaf fiber volume 0% (99,48 MPa ± 4,38), fraction volume 1% (131,40 MPa ± 5,39) and fraction volume 1,5% (148,88 MPa ± 3,74). One way ANOVA test showed that there was a significant difference in every group. Post Hoc test showed that there was a significant difference among groups.
Conclusion: The fraction of pineapple leaf fiber (Ananas Comosus L. Merr) volume affects to the flexural strength of flowable resin composite. Flowable resin composite fraction of pineapple leaf fiber volume 1,5% has the highest flexural strength.


Keywords


Flowable resin composite; Pineapple leaf fiber; Fiber reinforced composite; Volome fraction; Flexural strength

Full Text:

PDF

References


Mccabe, & Walls. (2014). Applied Dental Materials (EGC (Ed.); 9th Ed.). EGC.

Dhamayanti, I., & Nugraheni, T. (2013). Restorasi Fiber Reinforced Composite Pada Gigi Premolar Pertama Kanan Mandibula Pasca Perawatan Saluran Akar. Majalah Kedokteran Gigi Indonesia, 20(1), 65. Https://Doi.Org/10.22146/Majkedgiind.8382

Adi, H. N. S. (2017). Pengaruh Penambahan Serat Daun Nanas (Ananas Comosus L.Merr) Terhadap Kekuatan Fleksural Resin Komposit Flowable. Fakultas Kedokteran Gigi . Universitas Muhammadiyah Surakarta, 01, 1–7.

Murdiyanto, D., & Pratiwi, S. G. (2019). Pengaruh Penambahan Serat Kapas (Gossypium Sp.) Terhadap Kekuatan Fleksural Resin Komposit Flowable. JIKG (Jurnal Ilmu Kedokteran Gigi), 2(1), 1–5.

Septommy, C., Widjijono, W., & Dharmastiti, R. (2014). Pengaruh Posisi Dan Fraksi Volumetrik Fiber Polyethylene Terhadap Kekuatan Fleksural Fiber Reinforced Composite (The Effect Of Position And Volumetric Fraction Polyethylene Fiber On The Flexural Strength Of Fiber Reinforced Composite). Dental Journal (Majalah Kedokteran Gigi), 47(1), 52. Https://Doi.Org/10.20473/J.Djmkg.V47.I1.P52-56

Powers, J. ., & Sakaguchi, R. . (2012). Craig’s Restorative Dental Materials, 13th Edition. In British Dental Journal (Vol. 213, Issue 2). Https://Doi.Org/10.1038/Sj.Bdj.2012.659

Imam, D. (2015). Pengaruh Komposisi Glass Fiber Non Dental Dan Penambahan Silane Terhadap Kekuatan Geser Fiber Reinforced Composite Sebagai Retainer Ortodonsi. Majalah Kedokteran Gigi Indonesia, 1(1), 53–58.

Setyawan, P. D., Sari, N. H., & Putra, D. G. P. (2012). Pengaruh Orientasi Dan Fraksi Volume Serat Daun Nanas (Ananas Comosus) Terhadap Kekuatan Tarik Komposit Polyester Tak Jenuh. Dinamika Teknik Mesin, 2(1), 28–32.

Murdiyanto, D., & Kristi, R. (2020). Pengaruh Penambahan Serat Daun Nanas (Ananas Comosus (L.) Merr) Terhadap Kekuatan Tekan Resin Komposit Flowable. JIKG (Jurnal Ilmu Kedokteran Gigi), 3(1), 5–9.

Hidayat, P. (2008). Teknologi Pemanfaatan Serat Daun Nanas Sebagai Alternatif Bahan Baku Tekstil. Teknoin, 13(2), 31–35. Https://Doi.Org/10.20885/Teknoin.Vol13.Iss2.Art7

Todkar, S. S., & Patil, S. A. (2019). Review On Mechanical Properties Evaluation Of Pineapple Leaf Fibre (PALF) Reinforced Polymer Composites. Composites Part B: Engineering, Https://Doi.Org/10.1016/J.Compositesb.2019.106927

Wiguna, P. A., & Aji, M. P. (2015). Sifat Mekanik Komposit Cokelat Batang Dengan Filler Biji Mete. Indonesian Journal Of Mathematics And Natural Sciences, 37(2), 141–145.

Hadianto, E. (2013). Pengaruh Penambahan Polyethylene Fiber Dan Serat Sisal Terhadap Kekuatan Flek- Sural Dan Impak Base Plate Komposit Resin Akrilik. IDJ, 2(2), 57–67.

Hadianto, E., Syifa, L. L., & Hanafie, H. F. (2018). Pengaruh Fraksi Volume Fiber Sisal (Agave Sisalana) Terhadap Kekuatan Fleksural Resin Komposit. Odonto Dental Jurnal, 5, 139–144.

Wahyu, P., Deta, P., Pramana, Y., Surata, I. W., & Kusuma, I. (2020). Karakteristik Fisik Dan Mekanik Panel Biokomposit Serat Pelepah Pisang Resin Getah Pinus Variasi Waktu Perendaman Serat Dengan Naoh. Jurnal Ilmiah Teknik Desain Mekanika, 9(1), 840–845.

Chianelli-Junior, R., Reis, J. M. L., Cardoso, J. L., & Castro, P. F. (2013). Mechanical Characterization Of Sisal Fiber-Reinforced Recycled Hdpe Composites. Materials Research, 16(6), 1393–1397. Https://Doi.Org/10.1590/S1516-14392013005000128

Murdiyanto, D. (2017). Potensi Serat Alam Tanaman Indonesia Sebagai Bahan Fiber Reinforced Composite Kedokteran Gigi. Jurnal Material Kedokteran Gigi, 6(1), 14. Https://Doi.Org/10.32793/Jmkg.V6i1.260

Fatimina, A. D., Benyamin, B., & Fathurrahman, H. (2016). Pengaruh Posisi Serat Kaca (Fiberglass) Yang Berbeda Terhadap Kekuatan Fleksural Fiber Reinforced Acrylic Resin. ODONTO : Dental Journal, 3(2), 128. https://doi.org/10.30659/odj.3.2.128-132

Prasetyo, D., Raharjo, W. W., & Ubaidillah. (2013). Pengaruh Penambahan Coupling Agent Terhadap Kekuatan Mekanik Komposit Polyester-Cantula Dengan Anyaman Serat 3D Angle Interlock. Mekanika, 12(1), 44–52.




DOI: http://dx.doi.org/10.30659/medali.4.1.52-58

Refbacks

  • There are currently no refbacks.