In Vitro Study of Calcium Hydroxide Microencapsulation with Stichopus hermanii as Pulp Capping Material
DOI:
https://doi.org/10.30659/odj.12.2.198-207Keywords:
Microencapsulation, Sticopus hermanii, calcium hydroxide, pulp cappingAbstract
Background: Calcium hydroxide is a material that is widely used in pulp capping treatment. However, the use of this material causes tunnel defects due to the large absorption of calcium. This can be manipulated by creating an encapsulation formula. Stichopus hermanii is a marine biota that contains lots of hyaluronic acid and can be used as an encapsulation material which also plays a role in cell regeneration. The characteristics of the microencapsulated calcium hydroxide preparation with Stichopus hermanii as pulp capping material through an in vitro study.
Method: Stichopus hermanii was made freeze dry and dissolved with 1% acetic acid to obtain a gel concentration of 0.2%, 0.4%, and 0.8%. Next, calcium hydroxide powder is added with a ratio of 1: 6 and tripolyphospate (TPP) is added as a cross-linker agent and the mixture is stirred until homogeneous. The test material formed was subjected to SEM, PSA and cytotoxicity tests.
Result: The cytotoxicity test showed that all of the test materials (0.2%; 0.4%; 0.8%) were not toxic, especially at a concentration of 0.2%. The PSA test results indicate that this encapsulation shows the micro particle size formed. The SEM test shows a rough and stringy surface shape, where at a concentration of 0.2%, a smoother morphological formation is found.
Conclusion: The in vitro study showed that the microencapsulation of calcium hydroxide with Stichopus hermanii as a pulp capping material showed the characteristics of the non-toxic material, the micro size and the rough and fibrous surface shape.References
Garg, N., & Garg, A. 2015. Textbook of Operative Dentistry 3rd Edition. New Delhi: Jaypee Brothers Medical Publishers.
Hargreaves KM, Cohen S. 2016. Cohen’s pathways of the pulp. 17th ed. St Louis: Mosby Elsevier.
Tarigan, R. 2015. Karies Gigi. Edisi 2. EGC: Jakarta
Torabinejad, M., Walton, R. E., & Fouad, A. F. 2015. Endodontics Principles and Practice 5th Edition.pdf (Fifth Edit). St. Louis Mossouri: Elsevier Saunders.
Nurhayati, I. S., Kajian Pengendalian Mastitis Subklinis Melalui Pemberian Anbiotik pada Saat Kering Kandang di KPSBU Lembang Jawa Barat, Thesis, IPB University, 2014.
Mustafa, M., Jain, D., Taluka, S., Lecturer, S., Dentistry, C., & Capping, P. 2012. Role of Calcium Hydroxide in Endodontics : A Review. Global Journal of Medicine and Public Health, 1(1)
Baranwal, R., Singh, B., Dubey, A., & Avinash, A. 2016. Review Article Calcium Hydroxide in Dentistry. Chettinad Health City Medical Journal, 5(January), 30–33.
Mostafa, N., & Moussa, S. A. 2018. Mineral Trioxide Aggregate ( MTA ) vs Calcium Hydroxide in Direct Pulp Capping – Literature Review. Online Journal of Dentistru & Oral Health, 1(2), 1–6. https://doi.org/10.20431/2456-0030.0302004
Morotomi, T., Washio, A., & Kitamura, C. 2019. Current and Future Options for Dental Pulp Therapy. Japanese Dental Science Review, 55(1), 5–11. https://doi.org/10.1016/j.jdsr.2018.09.001
Albuntana, A., Yasman., dan Wardhana, W., 2011. Uji Toksisitas Ekstrak Empat Jenis Teripang Suku Holothuriidae dari Pulau Penjaliran Timur, Kepulauan seribu, Jakarta menggunakan Brine Shrimp Lethality Test (BSLT), Jurnal Ilmu Teknologi Kelautan Tropis, 3:65-72.
Collins, N., and Sulewski, C., 2011. Omega-3 fatty acids and wound healing. Nutrition 411, Ostomy Wound Management.
Sari RP, Budijono SCS. Characterization And Potency Of Stichopus Hermanii Ethanol Extract On Oral Wound Healing. Odonto Dental Journal, 2020; 7 (1) : 9-17
Gupta, A., and Dey, B. 2013. Microencapsulation for controlled drug delivery: a comprehensive review. Sunsari Technical College Journal, 1(1):48-54.
Hidayah N. 2016. Perbandingan Berbagai Teknik Mikroenkapsulasi Pakan dalam Menghasilkan Daging Sapi Sehat. Malang: SenasPro 2016 Universitas Muhammadiyah Malang, pp. 143- 151.
Astuti W.M., Dewi E.N., dan Kurniasih R. A., 2019. Pengaruh Perbedaan Jenis pelarut dan Suhu Pemanasan se;ama Ekstraksi terhadap Stabilitas Mikrokapsul Fikosianin dari Spirulina platensis. Jurnal Ilmu dan Teknologi Perikanan 1(1):8-14.
Nireesha, G., L. Divya, C. Sowmya, N. Venkateshan, M. Babu, and V. Lavakumar. 2013. Lyophilization/freeze drying: An review. World Journal of Pharmaceutical Research 4 (8):516–43.
Sari RP, Kusumawardani RP, Damaiyanti DW, Rahayu ARP, Sudjarwo SA. The Effectivity Of Scaffold From Anadara Granosa Shell-Stichopus Hermanii On Blood Vessel Counts After Tooth Extraction. Odonto Dental Journal, 2021; 8 (2) : 11-17.
Diana Soesilo, Aprilia, Moh.Basroni Rizal. InvitroMicro Encapsulation of Beta Tri Calcium Phosphate from Anadara granosa Shell Synthesis. Denta Jurnal Kedokteran Gigi, 2020; 14(2) : 71-76.
Freshney, R.I. 2010. Culture of Animal Cells: A Manual of Basic Technique and Specialized Applications. 6th Edition, John Wiley & Sons Ltd., Hoboken.
https://doi.org/10.1002/9780470649367
Ratna Putri*, Twi Agnita Cevanti**, Henu Sumekar. Sitotoksisitas Ekstrak Daun Mangrove Daruju(Acanthus Ilicifolius) Sebagai Bahan Irigasi Saluran Akar. Denta Jurnal Kedokteran Gigi, 2018; 12(1) : 44-50
Pannu R dan Berwal V. 2017. Calcium Hydroxide in Dentistry: A Review. Haryana: Journal of Applied Dental and Medical Sciences, 3(3), pp. 24-31.
Ziad NA. 2017. Calcium Hydroxide Liners – A Literature Review. Zababdeh: Clinical, Cosmetic, and Investigational Dentistry, 9, pp. 67-72.
Ahmadzadeh S, Herasaki Z, dan Zamanian A. 2011. Preparation and Characterisation of Calcium Phosphate – Hyaluronic Acid Nanocomposite Bone Cement. Tehran: Advances in Applied Ceramics Institute of Materials, Minerals, and Mining, 110(6), pp. 340-345.
Casale, M., Moffa, A., Vella, P., Sabatino, L., Capuano, F., Salvinelli, B., Salvinelli, F. 2016. Hyaluronic acid: Perspectives in dentistry. A systematic review. International Journal of Immunopathology and Pharmacology, 29(4), 572–582.
Imura, K., Hashimoto, Y., Okada, M., Yoshikawa, K., & Yamamoto, K. (2019). Application of hydroxyapatite nanoparticle-assembled powder using basic fibroblast growth factor as a pulp-capping agent. Dental Materials Journal, 38(5), 713–720. https://doi.org/10.4012/dmj.2018-198.
Lin, H. P., Tu, H. P., Hsieh, Y. P., & Lee, B. S. (2017). Controlled release of lovastatin from poly(lactic-co-glycolic acid) nanoparticles for direct pulp capping in rat teeth. International Journal of Nanomedicine, 12, 5473–5485. https://doi.org/10.2147/IJN.S138410.
Priyadarshini, B. M., Selvan, S. T., Narayanan, K., & Fawzy, A. S. (2017). Characterization of chlorhexidine-loaded calcium-hydroxide microparticles as a potential dental pulp-capping material. Bioengineering, 4(3). https://doi.org/10.3390/bioengineering4030059.
Downloads
Published
Issue
Section
License
Authors who publish with this journal agree to the following terms:
Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
This work is licensed under a Creative Commons Attribution 4.0 International License.