EFFECT OF SILANIZED TITANIUM DIOXIDE ON TENSILE STRENGTH OF SELF-CURED ACRYLIC RESIN
DOI:
https://doi.org/10.30659/medali.4.3.34-40Kata Kunci:
Titanium Dioxide (TiO2), self-cured acrylic resin, tensile strengthAbstrak
Background: Self-curing acrylic resin is a material used to make artificial tooth bases as well as reparate it when there is a fracture on the tooth bases. Titanium dioxide is one of the metal oxides that can be added to acrylic resins as an addition materials. This study aims to determine the effect of adding silanized titanium dioxide filler (TiO2) on tensile strength of self-cured acrylic resin.
Methods: This study is a true experimental laboratory study with the design post test only group design, using self-cured acrylic resin plates amounting to 24 plates measuring 165mm x 13mm x 3mm divided into groups of 4 with adding and without adding silanized TiO2. The self-cured acrylic resin plate mixed with silanized TiO2 was tested for tensile strength with a Universal Testing Machine. The data obtained were analyzed with Kruskal-Wallis test.
Results: There is an effect of adding titanium dioxide filler (TiO2) to the tensile strengthof self-cured acrylic resin with the highest tensile strength value at 26,1327 MPa ± 2,29608.
Conclusion: 5% titanium dioxide filler showed the highest tensile strength than other groups.
Referensi
Srivastava V, Dutt P, Chand P. Factors related to tooth loss among population : A cross sectional study. Int J Appl Dent Sci. 2018;4(3):31–3.
Campbell SD, Cooper L, Craddock H, Nattress B, Pavitt SH, Seymour DW. Removable partial dentures : The clinical need for innovation. J Prosthet Dent [Internet]. 2017;118(3):273–80. Available from: http://dx.doi.org/10.1016/j.prosdent.2017.01.008
Mohammad A, Aljafery A, Sayhood A, Abdulridha WM, Yousif AM. Evaluation the Tensile Strength of Cold-Cured Acrylic Resin Denture BaseMaterial by Adding Silver Nanoparticles. Indian J Public Heal Res Dev. 2018;9(10):951–5.
Ahmed MA, Althomali YM, Omar AA. Effect of Titanium Dioxide Nano Particles Incorporation on Mechanical and Physical Properties on Two Different Types of Acrylic Resin Denture Base. World J Nano Sci Eng. 2016;6(September):111–9.
Chen S, Yang J, Jia Y, Lu B. TiO 2 and PEEK Reinforced 3D Printing PMMA Composite Resin for Dental Denture Base Applications. Nanomaterial. 2019;9:1–18.
Fransisca W, Nasution ID. Pengaruh Penambahan Serat Kaca Dan Serat Poliester Terhadap Kekuatan Impak Bahan Basis Gigitiruan Resin Akrilik Polimerisasi Panas. B-Dent, J Kedokt Gigi Univ Baiturrahmah. 2018;2(1):16–22.
Srikavand S, Moslehifard E. Effect of TiO 2 Nanoparticles on Tensile Strength of Dental Acrylic Resins. J Dent Res Dent Clin Dent Prospects. 2014;8(4):197–203.
Alwan SA, Alameer SS. The Effect of the Addition of Silanized Nano Titania Fillers on Some Physical and Mechanical Properties of Heat Cured Acrylic Denture Base Materials. J Baghdad Coll Dent. 2015;27(1):86–91.
Chatterjee A. Properties improvement of PMMA using nano TiO2. J Appl Polym Sci. 2010;118(5).
Gad MM, Abualsaud R. Behavior of PMMA Denture Base Materials Containing Titanium Dioxide Nanoparticles : A Literature Review. Hindawi Int J Biomater. 2019;(January).
Tandra E, Wahyuningtyas E, Sugiatno E. The effect of nanoparticles TiO 2 on the flexural strength of acrylic resin denture plate. Padjadjaran J Dent. 2018;30(1):35–40.
Asar NV, Albayrak H, Korkmaz T, Turkyilmaz I. Influence of various metal oxides on mechanical and physical properties of heat-cured polymethyl methacrylate denture base resins. J Adv Prosthodont. 2013;5(3):241–7.
Aldabib JM, Ishak ZAM. Effect of hydroxyapatite filler concentration on mechanical properties of poly (methyl methacrylate) denture base. SN Appl Sci [Internet]. 2020;2(4):1–14. Available from: https://doi.org/10.1007/s42452-020-2546-1
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Authors who publish with this journal agree to the following terms:
Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
This work is licensed under a Creative Commons Attribution 4.0 International License.