THE INFLUENCE OF LEMON (Citrus Limon (L.)) IRON ION (Fe) REMOVAL ON STAINLESS STEEL ORTHODONTIC WIRE

Penulis

DOI:

https://doi.org/10.30659/medali.v3i1.16828

Kata Kunci:

Lemon, Stainless Steel Orthodontic Wire, Corrosion, Iron Ions (Fe)

Abstrak

Background: Lemons consist of 5-8% citric acid, have a pH of around 2.74. Drinks that have a critical pH of 5.5 can be said to be acidic drinks. Acidic drinks have the potential to cause corrosion of teeth and dental materials, one of which is stainless steel orthodontic wire. Stainless steel orthodontic wire is easily corroded, the wire has a composition of 71% Iron (Fe), 18% Chromium (Cr), 8% Nickel (Ni), and 0.2% Carbon (C). Corrosion is caused by the presence of inorganic components that act as electrolyte media that can trigger electrochemical reactions.
Method: Each sample was placed on each uninsulated petridish and labeled as a marker. This is done by inserting orthodontic wire which is immersed into the incubator for 3.5 hours at 37℃. Then the sample is taken and the separation between the sample and the solution is carried out. After that, the measurement of Iron (Fe) ions was carried out using the Atomic Absorption Spectrophotomery tool.
Result: The results showed the average release of Iron (Fe) ions in the experimental group of lemon juice with a concentration of 25% was 0.067mg/L, a concentration of 50% was 0.090mg/L and a concentration of 100% was 0.135mg/L. The test results obtained using the One Way Anova test showed that there was no significant difference (p>0.05).
Conclusion: There was no significant difference in the release of Iron (Fe) ions in stainless steel orthodontic wires between experimental groups, and there was no effect of soaking lemon juice (Citrus Limon (L.)) on the release of Iron (Fe) ions in stainless steel orthodontic wires.

Biografi Penulis

  • Chiquiteta Mariska Chairunnisa, Universitas Islam Sultan Agung
    Program Pendidikan Dokter Gigi Fakultas Kedokteran Gigi Universitas Islam Sultan Agung
  • R Rama Putranto, Universitas Islam Sultan Agung
    Departemen Orthodontic Fakultas Kedokteran Gigi Universitas Islam Sultan Agung
  • Moh Husnun Niam, Universitas Islam Sultan Agung
    Departemen Ilmu Kesehatan Gigi Masyarakat Fakultas Kedokteran Gigi Universitas Islam Sultan Agung

Referensi

Ardiyanti, A. (2018). Manfaat Lemon dalam Dunia Pertanian dan Kesehatan, (May), 1–3.

Harifah, I., Mustofa, A., & Suhartatik, N. (2017). Aktivitas Antioksidan Infused Water Dengan Variasi Jenis Jeruk (Nipis, Lemon, Baby) Dan Buah Tambahan (Stroberi , Anggur Hitam , Dan Kiwi), 1(1).

Hutasoit. (2005). Buah Segar Musim.

Kurniawati, A. C. (2014). Pengaruh perendaman infused water dan penyikatan

Wasono, N. P., Assa, Y. A., & Anindita, P. S. (2016). Pelepasan Ion Nikel Dan Kromium Bracket Stainless Stell Yang Direndam Dalam, 5(1), 158–163.

Kristianingsih, R., Joelijanto, R., Praharani, D., Gigi, F. K., & Unej, U. J. (2014). Analisis Pelepasan Ion Ni dan Cr Kawat Ortodontik Stainless Steel yang Direndam dalam Minuman Berkarbonasi ( Analysis of Ion Release Nickel and Chromium of Orthodontics Stainless Steel Wire Immersed by Carbonated Drink ).

Rotor, J. (2011). Sumarji, Jurnal ROTOR , Volume 4 Nomor1, Januari 2011 1, 4, 1–8.

Canina, L., & Pudyani, P. S. (2003). Pengaruh Kontaminasi Korosi.Pdf.

Iws, P., & Suparwitri, S. (2013). Sebelum Dan Setelah Perendaman Dalam Saliva Buatan Pada Periode Waktu Yang Berbeda ( Studi Laboratoris In Vitro ), 4, 136–141.

Fahlafi, R. (2019) Analisa Pengaruh Ph Lingkungan Terhadap Laju Korosi Dan Waktu Sisa Pada Heat Affected Zone Akibat Pengelasan Smaw Spec. Pipa Api 5l Grade B. Politeknik Perkapalan Negeri Surabaya.

Fahlafi, R. (2019) Analisa Pengaruh Ph Lingkungan Terhadap Laju Korosi Dan Waktu Sisa Pada Heat Affected Zone Akibat Pengelasan Smaw Spec. Pipa Api 5l Grade B. Politeknik Perkapalan Negeri Surabaya

Harmintaswa, I. (2020) Pelepasan Ion Fe (Ferrum) pada Kawat Stainless Steel Ortodonti yang Direndam Dalam Minuman Air Kelapa Kemasan. Universitas Jember.

Sharma, M. R. et al. (2018) ‘Effect of fruit juices and chloride ions on the corrosion behavior of orthodontic archwire’, Materials Technology. Taylor & Francis, pp. 1–7. doi: 10.1080/10667857.2018.1473992.

Sumule, I., Anindita, P.S., & Waworontu, O. A. (2015). Pelepasan Ion Nikel Dan Kromium Braket Stainless Steel Yang Direndam Dalam Minuman Berkarbonasi. Jurnal e-Gigi, 3(2): 464-468.

Unduhan

Diterbitkan

2021-09-28

Terbitan

Vol 3 No 1 (2021): Media Dental Intelektual September 2021

Bagian

Articles

Lisensi

Authors who publish with this journal agree to the following terms:

Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.

Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.

Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).

This work is licensed under a Creative Commons Attribution 4.0 International License.