THE DIFFERENCE IN COLOR CHANGE OF PREHEATED AND NON-PREHEATED NANOFILLER COMPOSITE RESIN AFTER IMMERSION IN NON-INSTANT AND INSTANT COFFEE

Sri Ainur Astutik, Benni Benyamin, Rosa Pratiwi

Abstract


Background: One of the aesthetic issues in using composite resin is the color change. This study aimed to compare the color changes of preheated and non-preheated nanofiller composite resin soaked in non-instant coffee and instant coffee.
Method: This study involved 24 round composite resins with a diameter of 12 mm and a thickness of 2 mm. The samples were divided into two groups (n=12); group I was prepared at 68°C and group II was prepared at room temperature. After curing, the samples were immersed in distilled water at 37°C for 24 hours before being measured with a UV-vis spectrophotometer. Each group was divided into two sub-groups (n=6), one soaked in non-instant coffee and the other in instant coffee for three days, and the final color was measured. The data was analyzed using two independent t-tests with a significance level of α =0.05.
Result: Two independent t-tests revealed a significant difference between preheated and non-preheated nanofiller composite resins soaked in non-instant coffee (p<0.05), as well as a significant difference between preheated and non-preheated nanofiller composite resins soaked in instant coffee (p<0.05).
Conclusion: The preheating was effective to improve the color stability of composite resin after immersion in non-instant coffee and instant coffee.


Keywords


Preheated; Composite Resin; Color Stability; Coffee

References


Manappallil JJ. Basic Dental Materials. 4th ed. New Delhi: Jaypee Brothers Medical Publisher; 2016.

Anusavice KJ, Shen C, Rawls HR. Phillips’ Science of Dental Materials. 12th ed. USA: Elsevier; 2013.

Hatrick CD, Eakle WS. Dental Materials: Clinical Applications for Dental Assistants. 3rd ed. St. Louis, Missouri: Elsevier; 2016.

Sakaguchi R, Ferracane J, Powers J. Craig’s Rstorative Dental Materials. Fourteenth. St. Louis, Missouri: Elsevier Inc.; 2019.

Khurshid Z, Najeeb S, Zafar MS, Sefat F. Advanced Dental Biomaterials [Internet]. United Kingdom: Elsevier; 2019. Available from: http://library1.nida.ac.th/termpaper6/sd/2554/19755.pdf

Raja KK, Hari P, Chin MQK, Singbal K, Fareez IM. Color Stability of a New Rice Husk Composite in Comparison with Conventional Composites after Exposure to Commonly Consumed Beverages in Malaysia. Int J Dent. 2019;2019:1–8.

Chittem J, Sajjan GS, Kanumuri MV. Spectrophotometric evaluation of colour stability of nano hybrid composite resin in commonly used food colourants in Asian countries. J Clin Diagnostic Res. 2017;11(1):ZC61–5.

Spina DRF, Grossi JRA, Cunali RS, Baratto Filho F, Cunha LF da, Gonzaga CC, et al. Evaluation of Discoloration Removal by Polishing Resin Composites Submitted to Staining in Different Drink Solutions. Int Sch Res Not. 2015;2015:1–5.

R Jaya Shree Roja NS, Prabhakar V, Minu K, Subha A, Ambalavanan P. Comparative evaluation of color stability of three composite resins in mouthrinse: An in vitro study. J Conserv Dent. 2019;22:175–80.

Mundim FM, Garcia LDFR, Cruvinel DR, Lima FA, Bachmann L, Pires-De-Souza FDCP. Color stability, opacity and degree of conversion of pre-heated composites. J Dent. 2011;39:25–9.

Aziz A, Al A, Saad S, Qasim B, Ramakrishnaiah R. Effect of different beverages on the color stability and degree of conversion of nano and microhybrid composites. Dent Mater J. 2013;32(2):326–31.

Darabi F, Seyed-Monir A, Mihandoust S, Maleki D. The effect of preheating of composite resin on its color stability after immersion in tea and coffee solutions: An in-vitro study. J Clin Exp Dent. 2019;11(12):1151–6.

Arora V, Arora P, Al Shammrani A, Fahmi MK. Devices & Methods for pre-heating/pre-warming Dental Resin Composites: A Critical Appraisal. Int J Oral Heal Med Res. 2017;4(2):52–5.

Kristanti Y. Perubahan warna resin komposit nanohibrida akibat perendaman dalam larutan kopi dengan kadar gula yang berbeda. J PDGI. 2016;65(1):26–30.

Diansari V, Ningsih DS, Arbie TA. Pengaruh Minuman Kopi Luwak Terhadap Perubahan Warna Resin Komposit Nanohibrid. Cakradonya Dent J. 2015;7(1):790–5.

Yang JNC, Raj JD, Sherlin H. Effects of preheated composite on micro leakage-an in-vitro study. J Clin Diagnostic Res. 2016;10(6):ZC36–8.

Borges BCD, Costa ES da, Sousa SEP, Arrais AB, Assunção IV de, Santos AJS dos. Preheating impact on the colour change of pit-and-fissure sealants after immersion in staining beverages. Int J Dent Sci Res [Internet]. 2015;2:64–8. Available from: http://dx.doi.org/10.1016/j.ijdsr.2015.11.002

Sousa SEP, da Costa ES, Borges BCD, de Assunção IV, dos Santos AJS. Staining resistance of preheated flowable composites to drinking pigmented beverages. Rev Port Estomatol Med Dent e Cir Maxilofac. 2015;56(4):221–5.

Abed Kahnamouei M, Gholizadeh S, Rikhtegaran S, Daneshpooy M, Kimyai S, Alizadeh Oskoee P, et al. Effect of preheat repetition on color stability of methacrylate- and silorane-based composite resins. J Dent Res Dent Clin Dent Prospects [Internet]. 2017;11(4):222–8. Available from: https://doi.org/10.15171/joddd.2017.039

Muliani SI. Perbedaan Perubahan Warna Resin Komposit Nano Hibrid Pada Perendaman Minuman Kopi Robusta Dan Kopi Bubuk Instan. 2018.

Nie J, Linde´nLA˚ . Rabek JF, Fouassier JP, Morlet-Savary F, Scigalski F et al. A reappraisal of the photopolymerization kinetics of triethyleneglycol dimethacrylate initiated by camphorquinone-N, N-dimethyl-p-toluidine for dental purposes. Acta Polym. 1998;49:145–61.

Soares-Geraldo D, Scaramucci T, Steagall-Jr W, Braga SRM, Sobral MAP. Interaction between staining and degradation of a composite resin in contact with colored foods. Braz Oral Res. 2011;25(4):369–75.

Afrida N. Perbedaan Kekasaran Permukaan Resin Komposit Nano Pada Perendaman Teh Hitam Dan Kopi. J Wiyata. 2015;2(1):48–53.

Annisa H, Pintadi H, Yogyakarta UM, Cara B. Pengaruh Konsentrasi Kopi Hitam Terhadap Perubahan Warna Pada Resin Komposit Hybrid. Insisiva Dent J. 2013;2(1):63–7.




DOI: http://dx.doi.org/10.30659/medali.4.2.123-129

Refbacks

  • There are currently no refbacks.